Product Description

NewPro solvent-based anti-adhesive coating for industrial application is an anorganic-organic product based on Nano-technology. The self-organizing anti-adhesive components create a very good roll-off effect against polaren and nonpolar liquids. Cleaning dirt and lime becomes easier.
Main application area: demoulding/dismantling (i.e. PU, PVC, epoxy resin). Anti-adhesive coating protecting against paint in paint finishing systems, print shops etc.

Demoulding/Dismantling (i. e., PU, PVC, epoxy resins), Anti-adhesive layer against paints in lacquer plant construction and the printing industry, etc…Material Basis:

• Solvent-based system with anti-adhesive components.

Color:

• Colorless.

PH-Value:

• Weak acid

Package Sizes:

• 1-L-PE Bottle 0.8 kg
• 5-L-PE Canister 3.6 kg
• 20-L-PE Canister 17.0 kg

Storage

Minimum of 12 months at temperatures between 5 and 35 degrees Celsius when stored in tightly sealed original container (light clouding of material possible). Protect against frost and higher temperatures. In the event of storage beyond expiration date/recommended period, test the material prior to use. Tightly air seal opened containers to preserve product life. Ensure sufficient ventilation in product storage areas.

Preparation

No preparation necessary – Material comes ready for use and application directly from the package.

Application

Apply a single continuous layer in spray with a criss-cross pattern. Application Temperatures

Material, Air temperature and surface: between + 5 and + 35 Degrees Celsius. Thermal hardening for 60 minutes at temperatures between 200 and 300 Degrees Celsius. Best adhesiveness and hardening at 300 Degrees Celsius. Deviations from this are possible, as external conditions can influence the hardening duration.

Use and Consumption

• Apply approximately 75 ml/m²

Safety and Protective Measures

During application and use, follow carefully the instructions and safety precautions on the package label, as well as the pertinent safety and accident instructions of appropriate occupational and trade associations. For further detailed instructions, see safety data sheets.

Cleaning of Tools

• Clean tools with alcohol or thinner.

Improvements and Second Coatings

Use abrasive finishing (ie., sandpaper) or through emplacement in a caustic potash / 2-Propanol bath.

Cleaning of Coated Surfaces

Due to the fact that the coated surface has a water and dirt repellent effect, only a mild cleaner is needed. Scouring cleaners and cleaners with extremely high pH values (<2 and >10) could adversely affect the performance of the coating material and, therefore, should not be used.

Disposal
Material residue and remains must be disposed of in accordance with local and state regulations for paints and lacquers.

Technical Data

Salt Spray (DIN EN ISO 9227 NSS): 1000h

Weathering DBL 7906: 15 min 23°C: 4h-30°C: 10 cycles 15 min 23°C: 4h 80°C: 30 min 40°C 98% rel. humidity.

Acid/Base Resistance: pH 2 to pH 10

Pencil Hardness: 7H

Taber test (CS10 F Roll; 11 mg1000 rotations per minute:

Temperature Resistance: Continuous up to 300 Degrees C.

Surface Energy: 12 MN/m